- Synthesis and Characterization of Poly (Styrene-b-vinyltrimethoxysilane) Block Copolymers
- 高分子通报 2013年26卷第3期页码：89-93
- 作者机构：
  
  常州大学材料科学与工程学院，常州　213164
- 作者简介：
  
  *张震乾(1973-)，男，江苏省江阴人，副教授，主要从事高分子材料科学研究，E-mail:zqzhang@cczu.edu.cn.
- 基金信息：
- DOI：
  中图分类号：
- 纸质出版日期：2013-03，
  
  收稿日期：2012-09-29，
  
  修回日期：2012-11-22，
扫描看全文
张震乾, 袁贵升, 吉祥, 何剑虹. 苯乙烯和乙烯基三甲氧基硅烷嵌段共聚物的制备及表征[J]. 高分子通报, 2013,26(3):89-93.

Zhen-qian ZHANG, Gui-sheng YUAN, Xiang JI, Jian-hong HE. Synthesis and Characterization of Poly (Styrene-b-vinyltrimethoxysilane) Block Copolymers[J]. Polymer Bulletin, 2013,26(3):89-93.
张震乾, 袁贵升, 吉祥, 何剑虹. 苯乙烯和乙烯基三甲氧基硅烷嵌段共聚物的制备及表征[J]. 高分子通报, 2013,26(3):89-93. DOI：

Zhen-qian ZHANG, Gui-sheng YUAN, Xiang JI, Jian-hong HE. Synthesis and Characterization of Poly (Styrene-b-vinyltrimethoxysilane) Block Copolymers[J]. Polymer Bulletin, 2013,26(3):89-93. DOI：

摘要

以苯乙烯(St)为单体

二硫代萘甲酸异丁腈酯(CPDN)为可逆-加成断裂链转移聚合(RAFT)试剂

合成大分子链转移剂

再加入不同质量的乙烯基三甲氧基硅烷(A171)

得到嵌段比不同的共聚物P(St-

-A171)。通过核磁共振谱仪

H-NMR、凝胶渗透色谱GPC、动态力学分析仪DMA和接触角等方法对P(St-

-A171)结构进行了表征。结果表明:随着

A171

嵌段比从1:0.15增加到1:0.45

P(St-

-A71)数均分子量从10400增加到14000

PDI指数从1.42增加到1.58;聚合物成膜后接触角由78.4°增加到89.6°。通过以上分析得出结论

RAFT合成嵌段共聚物的嵌段比对P(St-

-A171)性能有较大影响。

Abstract

The macromolecules chain transfer agent was synthesized by using styrene (St) as monomer and 2-cyanoprop-2-yl1-dithionaphthalate (CPDN) as RAFT agent. The different block ratio of copolymers P(St-

-A171) were synthesized by dvinyltrimethoxysilane (A171) and macromolecules chain transfer agent. The structure of block copolymer was characterized by

H NMR

gel permeation chromatography GPC

dynamic mechanical analysis (DMA) and other methods. The results showed that the number-average molecular weight of block polymer was increased from 10400 to 14000 and PDI index increased from 1.42 to 1.58 as the block ratio of

A171

increased from 1:0.15 to 1:0.45. The contact angle of block polymer film was increased from 78.4° to 89.6°. Through the analysis above

the

A171

block ratio have great influence on the performance of P (St-

-A171).

关键词

苯乙烯链转移剂乙烯基三甲氧基硅烷嵌段共聚物

Keywords

StyreneChain transfer agentVinyltrimethoxysilaneBlock copolymers

references

更多指标>

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

苯乙烯-间戊二烯交替共聚物环氧化研究

苯乙烯-对叔丁基苯乙烯-间戊二烯三元共聚物制备及表征

利用嵌段共聚物制备介孔材料的研究进展

（聚苯乙烯/有机蒙脱土）/聚丙烯酸正丁酯核壳纳米复合材料的制备

基于聚异戊二烯嵌段共聚物的研究进展