- 对甲酚修饰的超高交联树脂的合成及对4-硝基苯胺的吸附性能
- Synthesis of p-Cresol Modified Hypercrosslinked Resin and its Adsorption Performances for p-Nitroaniline
- 高分子通报 2013年26卷第5期页码：54-59
- 作者机构：
  
  湖南城市学院化学与环境工程学院，益阳　413000
- 作者简介：
  
  肖谷清，男，博士，副教授，主要从事功能高分子材料研究。E-mail : xiaoguqing@yahoo.com.cn.
- 基金信息：
  
  湖南省科技计划资助项目(2011SK3126);湖南省应用基础研究基地开放基金项目(湖科计字[2012] 154 号)
- DOI：
  中图分类号：
- 纸质出版日期：2013-05，
  
  收稿日期：2012-10-03，
  
  修回日期：2012-12-13，
扫描看全文
肖谷清. 对甲酚修饰的超高交联树脂的合成及对4-硝基苯胺的吸附性能[J]. 高分子通报, 2013,26(5):54-59.

Gu-qing XIAO. Synthesis of p-Cresol Modified Hypercrosslinked Resin and its Adsorption Performances for p-Nitroaniline[J]. Polymer Bulletin, 2013,26(5):54-59.
肖谷清. 对甲酚修饰的超高交联树脂的合成及对4-硝基苯胺的吸附性能[J]. 高分子通报, 2013,26(5):54-59. DOI：

Gu-qing XIAO. Synthesis of p-Cresol Modified Hypercrosslinked Resin and its Adsorption Performances for p-Nitroaniline[J]. Polymer Bulletin, 2013,26(5):54-59. DOI：

摘要

氯球和对甲基酚发生Friedel-Crafts反应制备对甲基酚修饰的超高交联树脂(简记为GQ-03)

研究 GQ-03树脂对4-硝基苯胺(PNA)的吸附性能。实验结果表明:GQ-03树脂的比表面积高达1154. 45m

树脂孔径分布在微孔(0〜2nm)、中孔(2〜50nm)区;GQ-03树脂对PNA的吸附性能优于商业NDA-88、NDA-99、 NDA-150、XAD-4和H103树脂;当溶液pH值在3. 1〜8. 0之间

GQ-03树脂对PNA的吸附量最大;GQ-03树脂对PNA的吸附量随温度的升高而降低

树脂对PNA的吸附等温线符合Freundlich模型;GQ-03树脂对 PNA的饱和吸附量为154. 41mg/mL

树脂可用8. 8BV 80%乙醇和lmol/L HC1混合溶液解吸

解吸率为 98. 82%。

Abstract

The objective of this work was to study the adsorption performances for p-nitroaniline onto the p-cresol hyper-cross-linked resin (denoted GQ-03). GQ-03 resin was synthesized with chloromethylated polystyrene and p-cresol by Friedel-Crafts reaction. Dichloroethane was used as solvent. The results showed that the BET surface area of GQ-03 resin was up to 1154. 45m

/g. Only microporous and mesoporous were present in GQ-03 resin and there were no macropores in the polymeric adsorbent. The adsorption property of p-nitroaniline onto the GQ-03 resin was superior to commercial NDA- 88 resin

NDA-99 resin

NDA-150 resin

XAD-4 resin and H103 resin. The maximum adsorption capacity of GQ-03 resin emerged the pH range of 3. 1-8. 0. The adsorption capacity of p-nitroaniline onto the GQ-03 resin increased with the increase of the temperature. The adsorption isotherms could be correlated to the Freundlich model. The saturated adsorption quantity of p-nitroaniline was up to 154. 41mg • mL

-1

. The resin could be desorbed with 8. 8BV 80% ethanol and lmol/L hydrochloric acid. The desorption rate was 98. 82%.

关键词

超高交联树脂对甲基酚4-硝基苯胺吸附

Keywords

Hyper-cross-linked resinp-Cresolp-NitroanilineAdsorption

references

更多指标>

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

超高交联树脂的功能基化及应用研究进展

基于吸附色谱的分级技术在聚烯烃表征中的应用

氢化松香基羟基化聚合物微球的制备及其对苯酚的吸附特性

硫化聚间氨基苯硫酚/淀粉复合材料的制备及其对Hg(Ⅱ)的高效吸附

农业废弃物制备活性炭的研究进展