原液着色阻燃共聚酯及其纤维的制备与表征

刘会超; 黄意龙; 龚静华; 马敬红; 杨曙光; 徐坚

您当前的位置：

首页 >

文章列表页 >

原液着色阻燃共聚酯及其纤维的制备与表征

研究简报 | 更新时间：2022-09-18

- 原液着色阻燃共聚酯及其纤维的制备与表征
- The Preparation and Characterization of Spun-dyed Flame Retardant Copolyester
- 高分子通报 2013年26卷第10期页码：179-183
- 作者机构：
  
  纤维材料改性国家重点实验室，材料科学与工程学院，东华大学，上海　201620
- 作者简介：
  
  刘会超(1985-)，男，博士，主要从事高分子结构与性能方面的研究
  *E-mail:mjh68@dhu.edu.cn.
- 基金信息：
- DOI：
  中图分类号：
- 纸质出版日期：2013-10，
  
  收稿日期：2013-07-23，
扫描看全文
刘会超, 黄意龙, 龚静华, 马敬红, 杨曙光, 徐坚. 原液着色阻燃共聚酯及其纤维的制备与表征[J]. 高分子通报, 2013,26(10):179-183.

Hui-chao LIU, Yi-long HUANG, Jing-hua GONG, Jing-hong MA, Shu-guang YANG, Jian XU. The Preparation and Characterization of Spun-dyed Flame Retardant Copolyester[J]. Polymer Bulletin, 2013,26(10):179-183.
刘会超, 黄意龙, 龚静华, 马敬红, 杨曙光, 徐坚. 原液着色阻燃共聚酯及其纤维的制备与表征[J]. 高分子通报, 2013,26(10):179-183. DOI：

Hui-chao LIU, Yi-long HUANG, Jing-hua GONG, Jing-hong MA, Shu-guang YANG, Jian XU. The Preparation and Characterization of Spun-dyed Flame Retardant Copolyester[J]. Polymer Bulletin, 2013,26(10):179-183. DOI：

摘要

采用原液着色技术制备了掺杂无机、有机染料的原液着色阻燃共聚酯切片

并对其可纺性及所得着色阻燃纤维性能进行了研究。通过差示扫描量热仪 (DSC)、热失重分析仪 (TGA)、极限氧指数仪 (LOI)、声速仪及纱线强伸度仪等对所得样品进行了表征测试。结果表明

染料的加入对阻燃共聚酯的结晶性能及热稳定性能影响很小

且原液着色阻燃共聚酯的LOI在33%~35%之间

呈现良好的阻燃性能。原液着色阻燃共聚酯切片具有很好的可纺性

热收缩测试表明染料掺杂阻燃共聚酯纤维的热收缩性能有所降低

尺寸稳定性有所提高

着色阻燃纤维的断裂强度能达到2.0 cN/dtex以上

可满足纺织品对纤维的强度要求。

Abstract

Coloring flame retardant copolyester with some inorganic and organic dyes was prepared by spun-dyed technology

and its spinnability was also studied. The crystallization properties

thermal behaviors

burning test and mechanical test of the coloring flame retardant copolyester were investigated by means of differential scanning calorimetry (DSC)

thermogravimetric analysis (TGA)

limiting oxygen index test (LOI) and yarn tensile strehgth tester. The results showed that the effects of dyes on the crystallization properties and thermal stability properties of flame retardant copolyester are negligible. Moreover

the coloring flame retardant copolyester showed a good flame retardant performance with LOI of 33%-35%. It also had a good spinnability. The thermal shrinkage of the coloring flame retardant copolyester fiber decreased

and the dimension stability improved. Its fracture strength can be more than 2.0 cN/dtex which can meet the requirement of textiles.

关键词

原液着色聚酯纤维阻燃力学性能

Keywords

Spun-dyedCopolyester fiberFlame retardantMechanical test