端羟基聚丁二烯/环氧氯丙烷合成多羟基聚丁二烯的实验研究

许文萍; 王香梅; 王萌霞

doi:10.14028/j.cnki.1003-3726.2017.04.008

您当前的位置：

首页 >

文章列表页 >

端羟基聚丁二烯/环氧氯丙烷合成多羟基聚丁二烯的实验研究

研究简报 | 更新时间：2022-09-06

- 端羟基聚丁二烯/环氧氯丙烷合成多羟基聚丁二烯的实验研究
- Studies on the Hydroxyl-terminated Poly butadiene/Epichlorohydrin Synthesis of Polyhydroxylated Polybutadiene
- 高分子通报 2017年30卷第4期页码：63-71
- 作者机构：
  
  中北大学化工与环境学院，太原 030051
- 作者简介：
  
  *E-mail：wangxiangmei@nuc.edu.cn.
- 基金信息：
- DOI：10.14028/j.cnki.1003-3726.2017.04.008
  中图分类号：
- 纸质出版日期：2017-04-01，
  
  收稿日期：2016-06-29，
  
  修回日期：2017-02-09，
扫描看全文
许文萍, 王香梅, 王萌霞. 端羟基聚丁二烯/环氧氯丙烷合成多羟基聚丁二烯的实验研究[J]. 高分子通报, 2017,30(4):63-71.

Wen-ping XU, Xiang-mei WANG, Meng-xia WANG. Studies on the Hydroxyl-terminated Poly butadiene/Epichlorohydrin Synthesis of Polyhydroxylated Polybutadiene[J]. Polymer Bulletin, 2017,30(4):63-71.
许文萍, 王香梅, 王萌霞. 端羟基聚丁二烯/环氧氯丙烷合成多羟基聚丁二烯的实验研究[J]. 高分子通报, 2017,30(4):63-71. DOI： 10.14028/j.cnki.1003-3726.2017.04.008.

Wen-ping XU, Xiang-mei WANG, Meng-xia WANG. Studies on the Hydroxyl-terminated Poly butadiene/Epichlorohydrin Synthesis of Polyhydroxylated Polybutadiene[J]. Polymer Bulletin, 2017,30(4):63-71. DOI： 10.14028/j.cnki.1003-3726.2017.04.008.

摘要

在氢氧化钠碱性条件下，以端羟基聚丁二烯(HTPB)和环氧氯丙烷（ECH)为原料，四丁基溴化铵 (TBAB)为催化剂，制得多羟基聚丁二烯(PHPB)。采用红外光谱(IR）、热重分析仪(TG)、核磁共振(

H-MNR)对原料、中间产物和产物的结构和热稳定性进行了分析。通过产品的羟值、粘度和产率详细考察了反应温度、反应时间、原料配比、催化剂用量和氢氧化钠用量对PHPB合成的影响。结果表明，最适宜合成工艺条件为：反应温度为 55℃ ，反应时间 1. 5h，

(HTPB)：

(ECH）：

(NaOH)：

(TBAB) = 1：2. 9：3：0. 03。

Abstract

Under the alkaline condition of sodium hydroxide

the polyhydroxylated polybutadiene (PHPB) was synthesized by hydroxyl terminated polybutadiene ( HTPB) and epichlorohydrin (ECH). Tetrabutyl ammonium bromide (TBAB) as the catalyst in this reaction. The structure and thermal stability of raw material

intermediate products and product were analyzed by Infrared spectroscopy (IR)

thermogravimetry (TG) and nuclear magnetic resonance (

H- MNR). The effect of reaction temperature

reaction time

raw material ratio

catalyst dosage and dosage of sodium hydroxide on the on the PHPB synthesis were investigated in detail by the hydroxyl value

viscosity and yield of the product. The result showed that the optimum synthesis conditions were as follows : reaction temperature was 55℃

reaction time was 1. 5h

(HTPB) :

(ECH) :

(NaOH) :

(TBAB) = 1:2. 9:3:0. 03.

关键词

多羟基聚丁二烯端羟基聚丁二烯环氧氯丙烷

Keywords

Polyhydroxylated polybutadieneHydroxyl terminated polybutadieneEpichlorohydrin