Study on Hydrolyzation and Enzymatic Degradation of Ciprofloxacin-polyurethane

更新时间：2022-09-18

- Study on Hydrolyzation and Enzymatic Degradation of Ciprofloxacin-polyurethane
- Polymer Bulletin Vol. 24, Issue 12, Pages: 87-91(2011)
- 作者机构：
  
  1.福州大学，化学化工学院，福州　350108
  2.福建医科大学，药学院，福州　350108
  3.宁德师范学院，化学与环境科学系，宁德　352100
- 作者简介：
- 基金信息：
- DOI：10.14028/j.cnki.1003-3726.2011.12.015
  CLC：
- Published：2011-12，
  
  Received：17 January 2011，
  
  Revised：29 April 2011，
扫描看全文
Zhi-guo WEN, Chun-yan LI, Cong-cong HU, Jian-hua HUANG, Sheng-xiong DONG. Study on Hydrolyzation and Enzymatic Degradation of Ciprofloxacin-polyurethane. [J]. Polymer Bulletin 24(12):87-91(2011)
DOI：

Zhi-guo WEN, Chun-yan LI, Cong-cong HU, Jian-hua HUANG, Sheng-xiong DONG. Study on Hydrolyzation and Enzymatic Degradation of Ciprofloxacin-polyurethane. [J]. Polymer Bulletin 24(12):87-91(2011) DOI： 10.14028/j.cnki.1003-3726.2011.12.015.

摘要

生物材料周围的感染和组织损伤是材料表面的黏附细菌引起的。为了阻止感染的发生

将环丙沙星共价结合到聚氨酯骨架中合成了环丙沙星-聚氨酯( CFPU) 抗菌材料。在37℃

pH =7.4 的PBS 缓冲溶液条件下

研究了CFPU 的降解情况

并对降解液的抗菌性能及细胞毒性进行了初步研究。研究结果表明

合成的 CFPU 在模拟正常体液环境下一个月内的药物损失在2%以内

较好地保留了药物。在胆固醇酯酶存在的条件下

药物的释放量明显大于空白实验

并且酶浓度的提高加剧了CFPU 中药物的释放

基本达到了控制释放的效果。抗菌实验结果显示

只有酶降解液具有抗菌活性

最低抑菌浓度(M IC) 为0.376μg/m L。细胞毒性实验表明降解液呈弱毒性

可以用于体内进行进一步的研究。

Abstract

The infection and tissue damage around the biomaterials are mainly caused by the bacterial adherence to the surface of the material. A new kind of antibacterial ciprofloxacin-polyurethane ( CFPU) was synthesized in order to prevent the infection. The degradation of CFPU in the phosphate-buffer saline ( PBS) ( pH =7.4

37 ℃) was studied. The antibacterial ability and the cytotoxicity of the degradation so lutions were assayed. The results showed that ciprofloxacin( CF) was kept effectively in CFPU while the drug loss was below 2% under the mimetic humoral condition. In the presence of cholesteral esterase( CE)

CF release was obviously larger than in the PBS only. Hence

the increase of the concentration of CE accelerated the release of CF

which indicated the control release ability of the material. The enzymatic degradation showed an ability to kill bacteria and the minimum inhibitory concentration ( MIC ) was measured as 0.376μg/mL. The degradation solutions were hypotoxicity according to the MTT assay.

关键词

抗菌控制释放聚氨酯环丙沙星降解胆固醇酯酶

Keywords

AntibacterialCont rol releasePolyurethaneCiprofloxacinDegradationCholesterol esterase

references

更多指标>

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Research Progress on in vivo Degradation and Metabolism Assessment of Carboxymethyl Chitosan-based Biomaterials

The Development of Electrospinning Technology in Medical Dressings

Advances in the Research of Materials Containing Catechol Groups in the Field of Antibacterial and Antifouling

Preparation and Properties of Flame Retardant and Antibacterial Wool Fabric

Preparation and Adsorption Behavior of Chelated Polyurethane Particles of Mercury Ions

Related Author

No data

Related Institution

State Key Laboratory of Molecular Vaccinology and Molecular Diagnostics,School of Public Health, Xiamen University

Xi’an Key Laboratory of Advanced Performance Materials and Polymers, Shaanxi University of Science and Technology

College of Bioresources Chemical and Materials Engineering, Shaanxi University of Science & Technology

Key Laboratory of Chemical Additives for China National Light Industry

College of Chemistry and Chemical Engineering, Shaanxi University of Science & Technology

⁰