The Preparation and Performance Research of A Novel Fluorinated Acrylate Copolymer Resin

Zi WANG; You FAN; Bin WANG; Chen ZHAN; Fa CHENG

doi:10.14028/j.cnki.1003-3726.2016.02.008

您当前的位置：

首页 >

文章列表页 >

The Preparation and Performance Research of A Novel Fluorinated Acrylate Copolymer Resin

更新时间：2022-09-12

- The Preparation and Performance Research of A Novel Fluorinated Acrylate Copolymer Resin
- Polymer Bulletin Vol. 29, Issue 2, Pages: 72-78(2016)
- 作者机构：
  
  天津大学理学院化学系，天津 300072
- 作者简介：
- 基金信息：
- DOI：10.14028/j.cnki.1003-3726.2016.02.008
  CLC：
- Published：20 February 2016，
  
  Received：02 July 2015，
  
  Revised：02 November 2015，
扫描看全文
Zi WANG, You FAN, Bin WANG, Chen ZHAN, Fa CHENG. The Preparation and Performance Research of A Novel Fluorinated Acrylate Copolymer Resin. [J]. Polymer Bulletin 29(2):72-78(2016)
DOI：

Zi WANG, You FAN, Bin WANG, Chen ZHAN, Fa CHENG. The Preparation and Performance Research of A Novel Fluorinated Acrylate Copolymer Resin. [J]. Polymer Bulletin 29(2):72-78(2016) DOI： 10.14028/j.cnki.1003-3726.2016.02.008.

摘要

以含氟丙烯酸酯与几种不同结构丙烯酸酯单体为原料

采用常规的自由基引发溶液聚合反应

制备了一种新型疏水低表面能丙烯酸树脂。并以水接触角和铅笔硬度两项指标考察其应用性能。经固化成膜后

聚合物膜与水的接触角达到118.5°

铅笔硬度达到F等级以上。系统研究了涂膜与水接触角和铅笔硬度的主要影响因素

可通过调节单体投料比来调控接触角和铅笔硬度来适应不同实际应用领域的技术指标需求。这种具有力学强度的疏水涂层具有很大的应用价值。

Abstract

In this article

a series of acrylate monomers with different structures

including a fluorinated acrylate

were utilized to synthesize a novel fluorinated acrylate copolymer resin by using free radical polymerization in solution. The water contact angle and pencil hardness of the resin film were determined to investigate its application performance. After being cured

the highest water contact angle and pencil hardness of the resin film was 118.5° and F level

respectively. Then the main influence factors of these two performances were studied. The hydrophobicity and hardness of the resin film could be controlled by simply adjusted the mass fraction of monomers. This hydrophobic coating with certain mechanical strength is concerned to have great application value.

关键词

含氟丙烯酸酯共聚物疏水性铅笔硬度

Keywords

Fluorinated acrylateCopolymerHydrophobicPencil hardness

references

更多指标>

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Temperature Rising Elution Fractionation and Fractions Characterization of PP/PB-1 in-reactor Alloy

Recent Progress in the Poly (lactic acid) Based Copolymers with Star-shaped or Dendritic Structures

New Progress on the Direct Synthesis of Polylactic Acid Copolymer

Recent Progresses in the Polymerization of Fluorinated Polymers via ATRP

Related Author

No data

Related Institution

Shandong Provincial Key Laboratory of Olefin Catalysis and Polymerization, Key Laboratory of Rubber-plastics(Ministry of Education), School of Polymer Science and Engineering, Qingdao University of Science and Technology

Shandong Provincial Key Laboratory of Olefin Catalysis and Polymerization, Key Laboratory of Rubber-plastics (Ministry of Education), School of Polymer Science and Engineering, Qingdao University of Science and Technology

Chambroad Chemical Industry Research Institute Co., Ltd.

Department of Chemistry,Tongji University

Institute of Nano-and Bio-polymeric Materials,School of Material Science and Engineering, Tongji University

⁰