Defect-free Epoxidized Trans-1,4-polyisoprene: New Synthetic Methodology and the Property of the Resulting Polymer

Jian JIANG; Rui-ying GONG; Wei YAO; Xiu-bo JIANG; Xiao-bo WAN

doi:10.14028/j.cnki.1003-3726.2017.02.009

您当前的位置：

首页 >

文章列表页 >

Defect-free Epoxidized Trans-1,4-polyisoprene: New Synthetic Methodology and the Property of the Resulting Polymer

更新时间：2022-09-06

- Defect-free Epoxidized Trans-1,4-polyisoprene: New Synthetic Methodology and the Property of the Resulting Polymer
- Polymer Bulletin Vol. 30, Issue 2, Pages: 64-73(2017)
- 作者机构：
  
  1.青岛科技大学橡塑材料与工程教育部重点实验室，青岛 266042
  2.中国科学院青岛生物能源与过程研究所生物基材料重点实验室，青岛 266101
- 作者简介：
- 基金信息：
- DOI：10.14028/j.cnki.1003-3726.2017.02.009
  CLC：
- Published：01 February 2017，
  
  Received：16 August 2016，
  
  Revised：29 November 2016，
扫描看全文
Jian JIANG, Rui-ying GONG, Wei YAO, Xiu-bo JIANG, Xiao-bo WAN. Defect-free Epoxidized Trans-1,4-polyisoprene: New Synthetic Methodology and the Property of the Resulting Polymer. [J]. Polymer Bulletin 30(2):64-73(2017)
DOI：

Jian JIANG, Rui-ying GONG, Wei YAO, Xiu-bo JIANG, Xiao-bo WAN. Defect-free Epoxidized Trans-1,4-polyisoprene: New Synthetic Methodology and the Property of the Resulting Polymer. [J]. Polymer Bulletin 30(2):64-73(2017) DOI： 10.14028/j.cnki.1003-3726.2017.02.009.

摘要

在水相悬浮法的基础上，采用实验室自制的环氧化剂在弱碱性条件下合成环氧化反式-1，4-聚异戊二烯（ETPI），并且对实验的条件进行了探索，对合成出的ETPI的结构与性能进行了研究。结果表明，在反应体系中加入适当的乙酸乙酯或氯仿可以提高环氧度。其中，加入乙酸乙酯的体系中最高可获得32%的环氧度，加入氯仿的体系最高可以获得51%的环氧度。相比于传统法（采用过氧甲酸或过氧乙酸作为环氧化剂），本合成法合成出的ETPI产品均一，不会像传统合成法那样发生开环、链断裂和呋喃环形成等副反应。采用该法制备的ETPI生胶的最大拉伸强度在20MPa以上，远高于用传统方法制备的ETPI生胶（近7倍）。对ETPI的性能测试表明，随着环氧度的升高，ETPI的抗湿滑性不断提高，而滚动阻力变化不大。耐油实验表明，当环氧度大于15%时，ETPI的耐油性有明显提升。

Abstract

This paper described a novel synthetic methodology towards epoxidized trans-1

4-poly isoprene (ETPI)

using a self-made oxidation reagent. Results showed that the addition of appropriate amount of ethyl acetate or chloroform to the reaction system could improve the degree of epoxidation. Epoxy degree as high as 32% in ethyl acetate

and 51% in chloroform could be obtained. Compared with the traditional method (using the peroxide or acetic acid as the oxidant)

the new synthetic method greatly suppressed the side reactions such as over oxidation

chain scission and furan ring formation

which in turn greatly improved the mechanical properties of the resulting ETPT. Mechanical tests shows that the raw ETPI prepared using this novel method shows a tensile strength over 20 MPa

almost 7 times stronger than ETPI prepared using traditional method. Improved wet-skid resistance was observed with the increase of epoxy degree for ETPI prepared using the new method

while rolling resistance changed little. Oil resistance tests showed that the oil resistance of ETPI was significantly increased when the epoxy degree was greater than 15%.

关键词

环氧化反式-14-聚异戊二烯环氧化反式-14-聚异戊二烯抗湿滑性耐油性

Keywords

Epoxidationtrans-14-PolyisopreneEpoxidized trans-14-polyisopreneWet-skid resistanceOil resistance

references

更多指标>

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

The Study of Epoxidation of Styrene/1,3-Pentadiene Alternating Copolymer

Modification of Trans-1, 4-poly(butadiene-co-isoprene) Copolymer Rubber (TBIR) with Environment-friendly Aromatic Oil (TDAE)

Research Progress on Epoxidized Natural Rubber Secondary Modified

Comparative Study on Isothermal Crystallization Hehaviors of Eucommia Ulmoide Gum and trans-1,4-Polyisoprene

Related Author

No data

Related Institution

College of Chemistry and Chemical Engineering, Hunan Institute of Science and Technology

China Petroleum and Chemical Corporation Baling Branch

Shandong Provincial Key Laboratory of Olefin Catalysis and Polymerization, Key Laboratory of Rubber-plastics of Ministry of Education, School of Polymer Science and Engineering, Qingdao University of Science and Technology

Shandong Huaju Polymer Material Co., Ltd.

Shandong Provincial Key Laboratory of Olefin Catalysis and Polymerization, Key Laboratory of Rubber-plastics (Ministry of Education), School of Polymer Science and Engineering, Qingdao University of Science and Technology

⁰