Three-dimensional Porous Scaffold Based on Poly(L-lactide acid) Polyvinylpyrrolid Fibers and Its Cellular Biocompatibility

Rui-lai LIU; Xiao-bao QI; Jin-yun ZHAO; Xing-ping FU

doi:10.14028/j.cnki.1003-3726.2019.04.006

您当前的位置：

首页 >

文章列表页 >

Three-dimensional Porous Scaffold Based on Poly(L-lactide acid) Polyvinylpyrrolid Fibers and Its Cellular Biocompatibility

更新时间：2022-09-02

- Three-dimensional Porous Scaffold Based on Poly(L-lactide acid) Polyvinylpyrrolid Fibers and Its Cellular Biocompatibility
- Polymer Bulletin Vol. 32, Issue 4, Pages: 40-47(2019)
- 作者机构：
  
  福建省生态产业绿色技术重点实验室，武夷学院生态与资源工程学院，武夷山 354300
- 作者简介：
- 基金信息：
- DOI：10.14028/j.cnki.1003-3726.2019.04.006
  CLC：
- Published：20 April 2019，
  
  Received：18 July 2018，
  
  Revised：25 October 2018，
扫描看全文
Rui-lai LIU, Xiao-bao QI, Jin-yun ZHAO, Xing-ping FU. Three-dimensional Porous Scaffold Based on Poly(L-lactide acid) Polyvinylpyrrolid Fibers and Its Cellular Biocompatibility. [J]. Polymer Bulletin 32(4):40-47(2019)
DOI：

Rui-lai LIU, Xiao-bao QI, Jin-yun ZHAO, Xing-ping FU. Three-dimensional Porous Scaffold Based on Poly(L-lactide acid) Polyvinylpyrrolid Fibers and Its Cellular Biocompatibility. [J]. Polymer Bulletin 32(4):40-47(2019) DOI： 10.14028/j.cnki.1003-3726.2019.04.006.

摘要

以四氢呋喃（THF）/水为共溶剂，在无其它添加剂条件下，通过低温淬火、萃取、洗涤和干燥得到PLLA/PVP纤维三维多孔支架。采用扫描电镜探讨THF/H

O比例、聚合物浓度、PLLA/PVP比例和淬火温度等条件对纤维支架形貌影响，通过水接触角、吸水率和体外生物活性等测试考察PVP添加对亲水性和生物活性影响。实验结果表明，纤维是由PLLA结晶所形成。PVP加入影响了PLLA结晶，但提高了纤维支架的亲水性。最佳的实验条件为THF/H

O=90 : 10、聚合物浓度9%（wt）、PLLA/PVP=90: 10、淬火温度一10℃，得到了直径为270±73nm均一、规整的纤维三维多孔支架，支架的吸水率、孔隙率和比表面积分别为17.29%、96.36%和13.45m

/g，该孔隙率和比表面积为细胞的粘附、迁移、分化、增殖以及养料的传输提供了很好的条件。

Abstract

Poly (L-lactide acid)/polyvinylpyrrolid three-dimensional nanofibers porous scaffold was prepared by low-temperature quenching

extraction

washing and drying from tetrahydrofuran/water co-solvent without the assistance of other additives. The effects of THF/H

O ratio

concentration

PLLA/PVP ratio and quenching temperature etc. on the morphology of fibrous scaffold were investigated by SEM. The influence of addition of PVP in water absorption and bioactivity were also investigated through water absorption test and in vitro bioactivity test. The results showed that fibrous scaffold was produced by crystallization of PLLA. The addition of PVP impeded the crystallization of PLLA and increased hydrophilia of fibrous scaffold. The optimum test conditions were as followed: THF/H

O=90 : 10

concentration 9%(wt)

PLLA/PVP=90 : 10 and quenching temperature -10℃

the uniform three-dimensional nanofibers porous scaffold with diameter of 270±73 nm were obtained. The water absorption

porosity and specific surface areas of fibrous scaffold were 17.29%

96.36% and 13.45m

respectively. High porosity and specific surface areas will offer good condition of cell adhesion

cell differentiation

cell prolifer and nutrients transport.

关键词

聚乳酸聚乙烯吡咯烷酮多孔支架热致相分离细胞相容性

Keywords

Poly(L-lactide acid)PolyvinylpyrrolidPorous scaffoldThermally induced phase separationCellular biocompatibility

references

更多指标>

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Preparation of Super-hydrophobic Polyurethane Porous Materials via Hexane Induction Method for Oil/Water Separation

Research Progress in Preparation and Application of Poly(4-methyl-1-pentene) Membranes

Preparation of Three-Dimensional Porous Scaffold Based on Poly (L-lactide acid) / Polycaprolactone Composites Nanofibers and Cellular Biocompatibility

Progress in Porous Scaffolds Fabricated by Porogen Leaching Method for Tissue Engineering

Polymeric Microporous Materials Formation via Thermally Induced Phase Separation Method

Related Author

No data

Related Institution

School of Materials and Chemical Engineering, Ningbo University of Technology

Beijing Key Laboratory of Membrane Materials and Engineering, Department of Chemical Engineering, Tsinghua University

School of Chemical and Environmental Engineering, China University of Mining and Technology

Department of Chemical and Environmental Engineering, Hubei University of Technology

Zhejiang Key Laboratory of Green Chemistry Synthesis Technology,College of Chemical Engineering and Material Science,Zhejiang University of Technology

⁰