Preparation and Properties of Crosslinked Polyamide Amide Gels Based on Hydrogen Bond Self-Repair

Yang LIU; Xiao-fei WANG; Chuan-ying SHI; Xiao-wen HUANG; Yan-yan WEI

doi:10.14028/j.cnki.1003-3726.2020.01.004

您当前的位置：

首页 >

文章列表页 >

Preparation and Properties of Crosslinked Polyamide Amide Gels Based on Hydrogen Bond Self-Repair

更新时间：2022-08-31

- Preparation and Properties of Crosslinked Polyamide Amide Gels Based on Hydrogen Bond Self-Repair
- Polymer Bulletin Vol. 33, Issue 1, Pages: 31-46(2020)
- 作者机构：
  
  青岛科技大学高分子科学与工程学院,青岛 266042
- 作者简介：
- 基金信息：
- DOI：10.14028/j.cnki.1003-3726.2020.01.004
  CLC：
- Published：20 January 2020，
  
  Received：20 September 2018，
  
  Revised：21 June 2019，
扫描看全文
Yang LIU, Xiao-fei WANG, Chuan-ying SHI, Xiao-wen HUANG, Yan-yan WEI. Preparation and Properties of Crosslinked Polyamide Amide Gels Based on Hydrogen Bond Self-Repair. [J]. Polymer Bulletin 33(1):31-46(2020)
DOI：

Yang LIU, Xiao-fei WANG, Chuan-ying SHI, Xiao-wen HUANG, Yan-yan WEI. Preparation and Properties of Crosslinked Polyamide Amide Gels Based on Hydrogen Bond Self-Repair. [J]. Polymer Bulletin 33(1):31-46(2020) DOI： 10.14028/j.cnki.1003-3726.2020.01.004.

摘要

通过试管倒立法和流变学测试对交联型聚酰胺胺凝胶的形成进行了判定。实验结果表明

直观的试管倒立法对聚酰胺胺凝胶形成的判定是有效的。通过对影响凝胶形成的各因素分析发现

在

=1.25、反应温度50℃、甲醇溶剂中制备的凝胶在单体质量浓度大于22%时能够形成凝胶

且符合IPN 凝胶的制备要求。通过对聚酰胺胺(PAMAM)、

-亚甲基双丙烯酰胺(MBA)和

-氨乙基哌嗪(AEPZ)的红外分析可以看出

本文中MBA 与AEPZ 可以发生交联反应

生成PAMAM

同时对加入LiBr的PAMAM 和未加入LiBr的PAMAM 红外分析表明

交联聚酰胺胺中含有丰富的氢键相互作用

为材料的自修复提供了可能。通过对PAMAM-1(单体质量浓度22%)、PAMAM-2(单体质量浓度27%)和PAMAM-3(单体质量浓度32%)的平衡溶胀率测试可以看出

PAMAM-1具有最大的溶胀率。通过对三者的动态模量测试

PAMAM-1、PAMAM-2和PAMAM-3的

'分别为5000Pa、15000Pa和24000Pa

说明凝胶具有良好的弹性。以PAMAM-3为例表征了材料的自修复过程

表明制备的交联型聚酰胺胺能够通过氢键及物理的相互作用对材料进行修复

在药物缓释等方面有潜在应用。

Abstract

The formation of polymer gels are judged by inverted test tube method and rheological test. The results show that these methods are effective during determining its formation. And according to the analysis of various factors affecting gel formation

it was found that the gels can be prepared when they are in the methanol solvent

R=1.25

50℃ and the monomer concentration (mass fraction) over 22%. Through the infrared analysis of polyamide amine (PAMAM)

-methylenebisacrylamide (MBA) and

-aminoethylpiperazine (AEPZ)

it shows that the chemical crosslinking reaction between MBA and AEPZ can be happened and PAMAM is then generated. And infrared analysis of PAMAM with LiBr and PAMAM with no LiBr showed that the cross-linked polyamide amine contained rich hydrogen bonds interaction

which provided a possibility for self-repair of the material. The equilibrium swelling ratio tests of PAMAM-1 (monomer concentration 22%)

PAMAM-2 (monomer concentration 27%) and PAMAM-3 (monomer concentration 32%) show that PAMAM-1 has the highest swelling ratio. Through the dynamic modulus tests

we know that the

' of PAMAM-1

PAMAM-2 and PAMAM-3 are 5000Pa

15000Pa and 24000Pa respectively

indicating that the gels had good elasticity and belonged to chemical crosslinking. The self-repairing process of the material was characterized by PAMAM-3

which indicated that the cross-linked polyamide amine can be repaired by hydrogen bonds and physical interaction

and has potential applications in drug release.

关键词

可逆非共价键氢键交联型聚酰胺胺凝胶自修复

Keywords

Reversible non-covalent bondHydrogen bondsCrosslinking polyamide amine gelsSelf-healing

references

更多指标>

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Preparation and Self-healing Properties of New Aliphatic Polycarbonate Elastomers with Physical Crosslinking and π-π-Conjugated Synergy

Experimental Design for Teaching Polymer Science for Sustainable Development: Preparation and Characterization of Repairable Thermoset Materials Containing Schiff Base Type Dynamic Covalent Bonds

Self-healing, Welding, Reprocessing Boronic Ester Vitrimers Based on Epoxidized Soybean Oil

Research Progress of Self-Healing Polymer Materials in Flexible Electronic Devices

Research on Multi-Responsive Shape Memory and Self-Healing Zwitterionic Polymer

Related Author

No data

Related Institution

Xiamen Key Laboratory of Intelligent Fishery, Xiamen Ocean Vocational College

Center for Molecular Science and Engineering, Northeastern University

Fujian Key Laboratory of Toxicant and Drug Toxicology, Medical College, Ningde Normal University

Center of Advanced Elastomer Materials, Beijing University of Chemical Technology

Polymer Science and Engineering Experiment Center, Beijing University of Chemical Technology

⁰