Effect of Urethane/Urea on Carbonyl Hydrogen Bonding of Polyester-Polyurethane Resin with Mixed TDI

ZHAO Yu-mei; ZHANG Bo; LIU Mei-qin; SHI Hong-cui

doi:10.14028/j.cnki.1003-3726.2023.03.009

您当前的位置：

首页 >

文章列表页 >

Effect of Urethane/Urea on Carbonyl Hydrogen Bonding of Polyester-Polyurethane Resin with Mixed TDI

更新时间：2023-01-16

- Effect of Urethane/Urea on Carbonyl Hydrogen Bonding of Polyester-Polyurethane Resin with Mixed TDI
- Polymer Bulletin Vol. 36, Issue 3, Pages: 355-365(2023)
- 作者机构：
  
  1.山西铁道职业技术学院，太原　030013
  2.山西省应用化学研究所(有限公司)，涂装高分子功能材料山西省重点实验室，太原　030027
- 作者简介：
- 基金信息：
- DOI：10.14028/j.cnki.1003-3726.2023.03.009
  CLC：
- Published：20 March 2023，
  
  Received：15 August 2022，
  
  Revised：20 September 2022，
扫描看全文
ZHAO Yu-mei, ZHANG Bo, LIU Mei-qin, SHI Hong-cui. Effect of Urethane/Urea on Carbonyl Hydrogen Bonding of Polyester-Polyurethane Resin with Mixed TDI. [J]. Polymer Bulletin 36(3):355-365(2023)
DOI：

ZHAO Yu-mei, ZHANG Bo, LIU Mei-qin, SHI Hong-cui. Effect of Urethane/Urea on Carbonyl Hydrogen Bonding of Polyester-Polyurethane Resin with Mixed TDI. [J]. Polymer Bulletin 36(3):355-365(2023) DOI： 10.14028/j.cnki.1003-3726.2023.03.009.

摘要

以聚己二酸-2-甲基-2

4戊二醇酯二醇(XCP-2000PM)为软段

以2

4-2

6混合甲苯二异氰酸酯(TDI

T-80)、异佛尔酮二胺(IPDA)和乙二醇(EG)、1

2-丙二醇(PG)、1

4-丁二醇(BDO)、新戊二醇(NPG)为硬段

制备了系列具有不同氨基甲酸酯基/脲键的聚酯型聚氨酯树脂

采用傅里叶变换红外光谱(FTIR)研究在总硬段含量不变的情况下

酯羰基、氨基甲酸酯基/脲键、混合甲苯二异氰酸酯结构对羰基氢键的影响。结果表明

在聚酯多元醇酯羰基的作用下

聚酯型聚氨酯树脂的氨酯羰基与酯羰基区红外光谱存在6个吸收峰

聚酯多元醇结构中的内部酯羰基不形成氢键

外部酯羰基部分形成氢键

氢键化程度随着小分子二元醇扩链比例的提高由5%升至9%。在硬段含量为20%时

聚酯型聚氨酯树脂以游离氨酯羰基与酯羰基为主

二者之和在60%左右。在2

4-2

6混合甲苯二异氰酸酯不对称结构的影响下

随着氨基甲酸酯基/脲键的增大

氨酯羰基与脲羰基的氢键化程度降低

游离氨酯羰基、酯羰基与脲羰基增多

微相分离程度减弱

软硬段混合程度增强;总体上脲羰基的氢键化程度所占比例较小

一般在6%左右;而P-PU 在扩链比例为0.25时

氨酯羰基的氢键化程度较大

而后减小。

Abstract

A series of different urethane/urea polyester polyurethanes (polyester-PU) with various diols were synthesized by poly(2-methyl-2

4-pentadiol adipate) diol as soft segment

4-2

6 mixed toluene diisocyanate (TDI T-80)

isophorone diamine (IPDA)

glycol (EG)

2-propylene glycol (PG)

4-butanediol (BDO) and neopentyl glycol as hard segment.Fourier transform infrared (FTIR) spectroscopy was used to investigate the effect of ester carbonyl

carbamate/urea linkages

and mixed toluene diisocyanate structures on carbonyl hydrogen bonding under the constant total hard segment content. The results showed that in the role of polyester polyol ester carbonyl group

there are six absorption peaks in the infrared spectra of urethane carbonyl and ester carbonyl region of polyester polyurethane resin. —C=O

int

not formed hydrogen bonds

and —C=O

ext

part formed hydrogen bonds

the degree of —C=O

ext

hydrogen bond increases from 5% to 9% with the increase of the chain extension ratio of small molecule diol. When the hard segment content of polyester polyurethane resin was about 20%

free urethane carbonyl and ester carbonyl were mainly 60%.With the increase of urethane/urea

under the combined influence of the asymmetric structure of 2

4-TDI

the degree of H-bonded urethane carbonyl and urea carbonyl in the polyester-PU decreased

free urethane carbonyl

ester carbonyl and urea carbonyl increased

which indicated that the microphase seperation of the polyester-PU was weakened

the mixing of soft and hard segments was enhanced. The degree of H-bonded urea carbonyl overall was a small proportion 6%.

was 0.25

the degree of H-bonded urethane carbonyl in P-PU was larger

and then decreased.

关键词

聚酯聚氨酯混合甲苯二异氰酸酯氨基甲酸酯基/脲键羰基氢键

Keywords

Polyester-polyurethaneMixed toluene diisocyanateRatio of urethane/ureaCarbonylHydrogen bond

references

更多指标>

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Carboxyl Nitrile Rubber Strengthened and Toughened by Supramolecular Polymer

Influences of 2-Substituent on Hydrogen Bonds and Properties of Polybenzoxazine Resins

Preparation and Mechanical Properties of High-strength PAM/PVP Semi-IPN Hydrogel

The Research and Development of Interpolymer Complexes

Synthesis,Structures and Applications of Hydrogen Bonded Supramolecular Polymers

Related Author

No data

Related Institution

School of Polymer Science and Engineering, Key Laboratory of Rubber-plastics of Ministry of Education, Qingdao University of Science and Technology

School of Petrochemical Engineering, Liaoning Petrochemical University

Key Laboratory of Science & Technology of Eco-Textile, Ministry of Education, School of Textiles and clothing, Jiangnan University

Deparment of Polymer Paterials, Materials Mnstitute of Shanghai University

State Key Laboratory of Polymer Physics and Polymer Chemistry, Changchun Institute of Applied Chemistry, Chinese Acdaemy of Sciences

⁰