微型注塑条件下POM/PEO/SiO<sub>2</sub>三元复合体系的充填行为

谭徜彬; 陈英红; 王琪

doi:10.14028/j.cnki.1003-3726.2015.11.006

您当前的位置：

首页 >

文章列表页 >

微型注塑条件下POM/PEO/SiO₂三元复合体系的充填行为

研究简报 | 更新时间：2022-09-18

- 微型注塑条件下POM/PEO/SiO₂三元复合体系的充填行为
- Filling Behavior of Polyoxymethylene/Poly(Ethylene Oxide)/SiO₂ Ternary Composite System under Microinjection Molding Conditions
- 高分子通报 2015年28卷第11期页码：42-49
- 作者机构：
  
  1.高分子材料工程国家重点实验室，四川大学高分子研究所，成都　610065
  2.四川理工学院分析测试中心，自贡　643000
- 作者简介：
  
  谭徜彬，(1981-)，男，博士，主要从事高分子复合材料制备和加工新技术研究
  *E-mail:smsyang135@163.com
- 基金信息：
  
  国家自然科学基金(51010004;51433006);高等学校学科创新引智计划(B13040)
- DOI：10.14028/j.cnki.1003-3726.2015.11.006
  中图分类号：
- 纸质出版日期：2015-11，
  
  收稿日期：2015-01-05，
  
  修回日期：2015-05-09，
扫描看全文
谭徜彬, 陈英红, 王琪. 微型注塑条件下POM/PEO/SiO₂三元复合体系的充填行为[J]. 高分子通报, 2015,28(11):42-49.

Chang-bin TAN, Ying-hong CHEN, Qi WANG. Filling Behavior of Polyoxymethylene/Poly(Ethylene Oxide)/SiO₂ Ternary Composite System under Microinjection Molding Conditions[J]. Polymer Bulletin, 2015,28(11):42-49.
谭徜彬, 陈英红, 王琪. 微型注塑条件下POM/PEO/SiO₂三元复合体系的充填行为[J]. 高分子通报, 2015,28(11):42-49. DOI： 10.14028/j.cnki.1003-3726.2015.11.006.

Chang-bin TAN, Ying-hong CHEN, Qi WANG. Filling Behavior of Polyoxymethylene/Poly(Ethylene Oxide)/SiO₂ Ternary Composite System under Microinjection Molding Conditions[J]. Polymer Bulletin, 2015,28(11):42-49. DOI： 10.14028/j.cnki.1003-3726.2015.11.006.

摘要

采用固相剪切碾磨技术制备了聚甲醛/聚氧化乙烯/二氧化硅(POM/PEO/SiO

)三元复合材料并实现其微型注塑加工

研究了POM/PEO/SiO

复合体系的微型注塑加工窗口、影响微型注塑加工过程充填行为的因素及其微型制品的复型行为.结果表明

POM/PEO/SiO

复合材料具有良好的微型注塑可加工性

根据其微型注塑加工窗口可获得复型良好的微型制品;POM/PEO/SiO

熔体在微型注塑过程中充模时间短

冷却速率快;注射速度和模腔温度对POM/PEO/SiO

体系的充填行为具有显著影响.此外

因纳米SiO

加入量较少

其对熔体充填行为的影响不大。

Abstract

The Polyoxymethylene/poly(ethylene oxide)/SiO

(POM/PEO/SiO

) ternary composite was prepared by solid state shear milling and then micro-injection molded.The microinjection molding (μIM) processing window

the factors that affect the filling behavior in the μIM process as well as the replication performance of the POM/PEO/SiO

composite micropart were studied. The experimental results indicated that the POM/PEO/SiO

system showed excellent μIM processability. The micropart with good replication was obtained according to the μIM processing window. The filling time was very short and the cooling speed was extremely high for the composite melt in the μIM process. The injection speed and the mold temperature had pronounced effect on the filling behavior of the melt. However

the effect of nano-SiO

on the filling behavior was not obvious due to the low nano-SiO

content.

关键词

聚甲醛聚氧化乙烯充填行为加工参数微型注塑

Keywords

PolyoxymethylenePoly(ethylene oxide)Filling behaviorProcessing parameterMicroinjection molding

references

更多指标>

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

高压下聚甲醛和聚氧化乙烯的熔融温度测量

PEO分子量对POM/PEO晶/晶共混物溶液结晶的影响

弹性体共混改性对聚甲醛结晶行为及力学性能的影响

聚乙烯醇/纳米羟基磷灰石复合材料微型注塑研究

聚甲醛的改性研究进展

微型注塑条件下POM/PEO/SiO2三元复合体系的充填行为

Filling Behavior of Polyoxymethylene/Poly(Ethylene Oxide)/SiO2 Ternary Composite System under Microinjection Molding Conditions

DOI：10.14028/j.cnki.1003-3726.2015.11.006

摘要

Abstract

关键词

Keywords

references

微型注塑条件下POM/PEO/SiO₂三元复合体系的充填行为

Filling Behavior of Polyoxymethylene/Poly(Ethylene Oxide)/SiO₂ Ternary Composite System under Microinjection Molding Conditions