含双噻唑基聚合物的合成及电流变性能研究

宋欣荣; 林原斌

doi:10.14028/j.cnki.1003-3726.2005.02.013

您当前的位置：

首页 >

文章列表页 >

含双噻唑基聚合物的合成及电流变性能研究

研究简报 | 更新时间：2022-09-18

- 含双噻唑基聚合物的合成及电流变性能研究
- Synthesized and Electrorheological Characteristics of Polymer Containing Bithiazole Group
- 高分子通报 2005年18卷第2期页码：88-92
- 作者机构：
  
  1.湘潭大学高分子材料研究所，湘潭　411105
  2.．湖南工程学院化学化工系，湘潭　411104
- 作者简介：
  
  宋欣荣（1955－），男，教授，主要从事功能高分子材料的合成与研究； E-mail：songxinrong＠vip.sina.com
- 基金信息：
  
  湖南省教育厅资助课题(01C448)
- DOI：10.14028/j.cnki.1003-3726.2005.02.013
  中图分类号：
- 纸质出版日期：2005-04，
扫描看全文
宋欣荣, 林原斌. 含双噻唑基聚合物的合成及电流变性能研究[J]. 高分子通报, 2005,18(2):88-92.

Xin-rong SONG, Yuan-bin LIN. Synthesized and Electrorheological Characteristics of Polymer Containing Bithiazole Group[J]. Polymer Bulletin, 2005,18(2):88-92.
宋欣荣, 林原斌. 含双噻唑基聚合物的合成及电流变性能研究[J]. 高分子通报, 2005,18(2):88-92. DOI： 10.14028/j.cnki.1003-3726.2005.02.013.

Xin-rong SONG, Yuan-bin LIN. Synthesized and Electrorheological Characteristics of Polymer Containing Bithiazole Group[J]. Polymer Bulletin, 2005,18(2):88-92. DOI： 10.14028/j.cnki.1003-3726.2005.02.013.

摘要

采用2，2′-二氨基-4，4′-双噻唑与联苯胺合成一种含有双噻唑基的共轭聚合物，通过红外、扫描电镜、热重分析等测试了该物质的结构及热稳定性等，并通过将聚合物分别分散在硅油和溴代二苯甲烷中制备电流变体，测试其电流变性能。结果表明：含双噻唑基的共轭聚合物作为电流变体的分散相表现出了良好的电流变性能，同时发现分散相和分散介质的密度相近时有利于电流变性能的提高。

Abstract

Polymer particles containing bithiazole group were synthesized with2

2-diamino-4

4-bithiazole and benzidine. The particles were characterized with FT-IR spectroscopy

thermogravi metric analysis and scanning electron microscopy. Electrorheological (ER) fluids were prepared by disperse the polymer into two different media of bromodiphenylmethane and silicone oil respecti vely. Rheological properties of the ER fluids were measured with a rotational rheometer. Effects of electric field strength

disperse phase concentration and different disperse medium on the ER fluids were measured and discussed. The results showed that ER behaviour was enhanced with an increase in the disperse phase concentration and in the electric field strength. ER behaviour with density match is better than that with density mismatch between disperse phase and disperse medium.

关键词

合成共轭聚合物双噻唑基电流变性能

Keywords

SynthesisConjugated polymerBithiazole groupER behaviour