- 离子凝胶反应法制备壳聚糖/N,O-羧甲基壳聚糖微球
- Preparation of Chitosan/N,O-carboxymethyl Chitosan Microspheres by Ionically Cross-linking Method
- 高分子通报 2005年18卷第6期页码：84-89
- 作者机构：
  
  天津大学材料科学与工程学院，天津　300072
- 作者简介：
  
  刘峻，27岁，男，硕士研究生，从事生物医用材料研究；
  *电话：022－27402702，E-mail：xbyuan@eyou.com
- 基金信息：
  
  国家自然科学基金青年基金资助项目(50301008)
- DOI：10.14028/j.cnki.1003-3726.2005.06.014
  中图分类号：
- 纸质出版日期：2005-12，
扫描看全文
刘峻, 原续波, 安超, 侯信, 盛京. 离子凝胶反应法制备壳聚糖/N,O-羧甲基壳聚糖微球[J]. 高分子通报, 2005,18(6):84-89.

Jun LIU, Xu-bo YUAN, Chao AN, Xin HOU, Jing SHENG. Preparation of Chitosan/N,O-carboxymethyl Chitosan Microspheres by Ionically Cross-linking Method[J]. Polymer Bulletin, 2005,18(6):84-89.
刘峻, 原续波, 安超, 侯信, 盛京. 离子凝胶反应法制备壳聚糖/N,O-羧甲基壳聚糖微球[J]. 高分子通报, 2005,18(6):84-89. DOI： 10.14028/j.cnki.1003-3726.2005.06.014.

Jun LIU, Xu-bo YUAN, Chao AN, Xin HOU, Jing SHENG. Preparation of Chitosan/N,O-carboxymethyl Chitosan Microspheres by Ionically Cross-linking Method[J]. Polymer Bulletin, 2005,18(6):84-89. DOI： 10.14028/j.cnki.1003-3726.2005.06.014.

摘要

以一氯乙酸与壳聚糖反应形成

N，O

-羧甲基壳聚糖两性聚电解质，分光光度法测定其等电点IEP＝ 2.86。以此两性聚电解质与壳聚糖可以在一定条件下形成微球，光学显微镜和电子显微镜测试表明，控制两种聚电解质配比可以制备不同粒径大小的微球，而超声功率对微球粒径的影响较小。红外光谱测试表明微球中

N，O

-羧甲基壳聚糖羧基以羧酸根形式存在，分光光度与电导法联合测定表明两种聚电解质以离子凝胶作用形成微球，其最佳制备条件为IEP（CM-CHITOSAN）

pKa（CS），在此较宽的pH 值范围内微球可稳定存在。

Abstract

Chitosan microspheres were prepared by ionically cross-linked chitosan with amphoteric

-carboxymethyl chitosan(CM-chitosan).CM-chitosan with a isoelectric point (IEP)2.86 was synthesized by chemical reacting chitosan with monochloroacetic acid

and the chemical structure was analyzed by IR and

C NMR.By adding CM-chitosan into chitosan solution

microspheres were formed instantaneously

and the structure of microspheres was characterized by IR and microscopy.The observation of optical microscopy

scanning electron microscopy and transmission electron microscopy showed that the ratio of chitosan to CM-chitosan had more influence on morphology and size of the microspheres than ultrasonic power

indicating that the charge action between this two polyelectrolytes were the mechanism of microsphere formation.This mechanism was also confirmed by measurement the change of absorbance and conductivity with pHvalue of chitosan/CM-chitosan solution

the result also showed that the pH range for microsphere formation is IEP

(CM-chitosan)

pKa

(chitosan)

关键词

壳聚糖羧甲基壳聚糖离子凝胶反应微球

Keywords

ChitosanNO-carboxymethyl chitosanIonically cross-linkMicrosphere

references

更多指标>

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

壳聚糖作为药物缓释载体的研究进展

淫羊藿苷壳聚糖/明胶微球的制备及其体外释放研究

聚丙烯酸/氧化石墨烯-壳聚糖复合膜的制备及其对染料的吸附分离

二氧化碳辅助壳聚糖/银凝胶小球的制备及其催化性能的研究

羧甲基壳聚糖基生物医用材料降解代谢行为的研究进展

离子凝胶反应法制备壳聚糖/N,O-羧甲基壳聚糖微球

Preparation of Chitosan/N,O-carboxymethyl Chitosan Microspheres by Ionically Cross-linking Method

DOI：10.14028/j.cnki.1003-3726.2005.06.014

摘要

Abstract

关键词

Keywords

references