溴化环氧/Novolacs 体系在CEM-3板中的应用

陈立新; 缪桦; 宋家乐; 景晨丽

doi:10.14028/j.cnki.1003-3726.2007.03.005

您当前的位置：

首页 >

文章列表页 >

溴化环氧/Novolacs 体系在CEM-3板中的应用

研究简报 | 更新时间：2022-09-18

- 溴化环氧/Novolacs 体系在CEM-3板中的应用
- The Application of Epoxy Bromide/Novolacs in CEM-3Copper Clad Laminate
- 高分子通报 2007年20卷第3期页码：30-36
- 作者机构：
  
  西北工业大学理学院应用化学系，西安　710072
- 作者简介：
  
  *陈立新，Tel：13227050810，E-mail：lixin@nwpu.edu.cn.
- 基金信息：
  
  西安应用材料创新基金资助(XA-AM-200510)
- DOI：10.14028/j.cnki.1003-3726.2007.03.005
  中图分类号：
- 纸质出版日期：2007-03，
扫描看全文
陈立新, 缪桦, 宋家乐, 景晨丽. 溴化环氧/Novolacs 体系在CEM-3板中的应用[J]. 高分子通报, 2007,20(3):30-36.

Li-xin CHEN, Hua MIAO, Jia-le SONG, Chen-li JING. The Application of Epoxy Bromide/Novolacs in CEM-3Copper Clad Laminate[J]. Polymer Bulletin, 2007,20(3):30-36.
陈立新, 缪桦, 宋家乐, 景晨丽. 溴化环氧/Novolacs 体系在CEM-3板中的应用[J]. 高分子通报, 2007,20(3):30-36. DOI： 10.14028/j.cnki.1003-3726.2007.03.005.

Li-xin CHEN, Hua MIAO, Jia-le SONG, Chen-li JING. The Application of Epoxy Bromide/Novolacs in CEM-3Copper Clad Laminate[J]. Polymer Bulletin, 2007,20(3):30-36. DOI： 10.14028/j.cnki.1003-3726.2007.03.005.

摘要

分别以PN、BPFN 和BPAN 为溴化环氧A80的固化剂，以DMP-30、HMTA 和2-MZ 为促进剂制备CEM-3覆铜板，研究了这三种线型酚醛树脂作为固化剂对CEM-3覆铜板力学性能、电性能、吸水性和耐热性等的影响。结果表明，以三种线型酚醛树脂为固化剂制备的CEM-3覆铜板的力学性能相近，而吸水性由高至低的顺序为 PN

BPFN

BPAN，介电性能由高至低的顺序为BPFN≈BPAN

PN，T

由高至低的顺序为PN

BPFN

BPAN。由BPAN 和BPFN 为固化剂制备的CEM-3覆铜板经150℃/2h 后处理，耐变色性明显优于PN 为固化剂制备的 CEM-3覆铜板。

Abstract

CEM-3 copper clad laminates (CCL) were made from epoxy bromide A80

curing agents of phenolic novolac (PN)

bisphenol F novolac (BPFN) and bisphenol A novolac (BPAN) with accelerants of DMP-30

HMTA and 2-MZ. The effects of these three novolacs on the properties of CEM-3CCL

such as mechanical properties

electrical properties

water absorbance and heat resistance

were discussed. The results show that the mechanical properties of CEM-3CCL fabricated by the three novolacs don’t have distinguished difference. The water absorbance

dielectric properties and T

of CEM-3CCL from high to low are PN

BPFN

BPAN

BPFN≈BPAN

PN and PN

BPFN

BPAN

respectively. The color–changing resistance of CEM-3CCL fabricated by BPFN and BPAN employed as curing agents is superior to that of CEM-3CCL fabricated by PN under the condition of 150℃/2h post-treatment.

关键词

CEM-3覆铜板线型酚醛树脂性能

Keywords

CEM-3 copper clad laminatesNovolacsProperties