四配位硅与甲基丙烯酸β-羟乙酯共聚物的制备及其结构表征

宋建华; 张建华; 徐敏; 董文; 郭仕恒

doi:10.14028/j.cnki.1003-3726.2007.03.006

您当前的位置：

首页 >

文章列表页 >

四配位硅与甲基丙烯酸β-羟乙酯共聚物的制备及其结构表征

研究简报 | 更新时间：2022-09-18

- 四配位硅与甲基丙烯酸β-羟乙酯共聚物的制备及其结构表征
- Preparation and Characterization of Copolymer from Styryl-tetra-coordinated Silicon Monomer and HEMA
- 高分子通报 2007年20卷第3期页码：37-40
- 作者机构：
  
  广州大学化学化工学院化学系，广州　510006
- 作者简介：
  
  宋建华（1967－），女，博士后、副教授，从事功能聚合物的合成，E-mail：sjhfsfyy@163.com.
- 基金信息：
  
  广东省自然科学基金资助项目(04300005)
- DOI：10.14028/j.cnki.1003-3726.2007.03.006
  中图分类号：
- 纸质出版日期：2007-03，
扫描看全文
宋建华, 张建华, 徐敏, 董文, 郭仕恒. 四配位硅与甲基丙烯酸β-羟乙酯共聚物的制备及其结构表征[J]. 高分子通报, 2007,20(3):37-40.

Jian-hua SONG, Jian-hua ZHANG, Min XU, Wen DONG, Shi-heng GUO. Preparation and Characterization of Copolymer from Styryl-tetra-coordinated Silicon Monomer and HEMA[J]. Polymer Bulletin, 2007,20(3):37-40.
宋建华, 张建华, 徐敏, 董文, 郭仕恒. 四配位硅与甲基丙烯酸β-羟乙酯共聚物的制备及其结构表征[J]. 高分子通报, 2007,20(3):37-40. DOI： 10.14028/j.cnki.1003-3726.2007.03.006.

Jian-hua SONG, Jian-hua ZHANG, Min XU, Wen DONG, Shi-heng GUO. Preparation and Characterization of Copolymer from Styryl-tetra-coordinated Silicon Monomer and HEMA[J]. Polymer Bulletin, 2007,20(3):37-40. DOI： 10.14028/j.cnki.1003-3726.2007.03.006.

摘要

以二氧化硅为起始原料，与乙二醇、氢氧化钾反应，生成高活性的五配位硅钾化合物。以此为原料，与对苄氯苯乙烯反应，制得含双键官能团的四配位硅单体。然后与甲基丙烯酸β-羟乙酯进行自由基共聚合，得到含硅支链的共聚物。最后用IR、EA、EDS、TG、DSC、GPC 等对四配位硅单体及其共聚物作了结构表征。IR 表明，四配位硅单体在1630cm－1附近的C＝C 伸缩振动吸收峰在共聚物中消失。TG 表明，共聚物在343℃开始分解。分子链间通过羟基可以交联成体型结构，具有不溶不熔的特性。用DSC 测得共聚物的玻璃化温度为 48.1℃。

Abstract

High reactive penta-coordinated organic silicon was prepared via the reaction of silica with ethylene glycol and potassium hydroxide. Tetra-coordinated silicon monomer with a double bond was produced by the reaction of this penta-coordinated silicon with 4-vinylbenzyl chloride. Then the copolymer with silicon-containing branch was prepared. by the free radical polymerization of this tetra-coordinated silicon monomer with HEMA. The tetracoordinated silicon monomer and its copolymer were characterized by FTIR

EDS

DSC

GPC

etc. An adsorption band of IR spectrum at 1630cm

-1

for C=C was indicated for tetra-coordinate silicon monomer

but disappeared for the copolymer. TG analysis showed the co-polymer began losing weight at 343℃. The glass transition temperature was 48.1℃.

关键词

配位硅化合物自由基聚合甲基丙烯酸β-羟乙酯

Keywords

Tetra-coordinated siliconFree radical polymerizationHEMA