- 高强度PAM/PVP半互穿网络凝胶制备及力学性能
- Preparation and Mechanical Properties of High-strength PAM/PVP Semi-IPN Hydrogel
- 高分子通报 2015年28卷第3期页码：61-67
- 作者机构：
  
  江南大学纺织服装学院，生态纺织教育部重点实验室，无锡　214122
- 作者简介：
  
  黎亚丽(1990-)，女，硕士研究生，研究方向为新型纺织化学品及其机理研究
  *E-mail:wchaoxia@sohu.com.
- 基金信息：
  
  国家自然科学基金(21174055);333高层次人才培养工程(BRA2011184);六大人才高峰高层次人才项目(2012-XCL-007)
- DOI：10.14028/j.cnki.1003-3726.2015.03.008
  中图分类号：
- 纸质出版日期：2015-03，
  
  收稿日期：2014-06-16，
  
  修回日期：2014-10-03，
扫描看全文
黎亚丽, 郭宁, 王潮霞, 殷允杰. 高强度PAM/PVP半互穿网络凝胶制备及力学性能[J]. 高分子通报, 2015,28(3):61-67.

Ya-li LI, Ning GUO, Chao-xia WANG, Yun-jie YIN. Preparation and Mechanical Properties of High-strength PAM/PVP Semi-IPN Hydrogel[J]. Polymer Bulletin, 2015,28(3):61-67.
黎亚丽, 郭宁, 王潮霞, 殷允杰. 高强度PAM/PVP半互穿网络凝胶制备及力学性能[J]. 高分子通报, 2015,28(3):61-67. DOI： 10.14028/j.cnki.1003-3726.2015.03.008.

Ya-li LI, Ning GUO, Chao-xia WANG, Yun-jie YIN. Preparation and Mechanical Properties of High-strength PAM/PVP Semi-IPN Hydrogel[J]. Polymer Bulletin, 2015,28(3):61-67. DOI： 10.14028/j.cnki.1003-3726.2015.03.008.

摘要

以过硫酸铵为引发剂通过一步溶液聚合制备了由化学交联的聚丙烯酰胺(PAM)与聚乙烯吡咯烷酮(PVP)贯穿形成的PAM/PVP半互穿网络(semi-IPN)凝胶

着重研究了凝胶的机械性能。红外光谱、热重分析及拉伸实验分析可知PAM与PVP之间存在氢键作用。拉伸实验表明:在PAM中引入PVP

凝胶拉伸强度明显提高

m(PVP)/m(AM)=7.51%时制备的PAM/PVP semi-IPN凝胶拉伸强度比单纯化学交联的PAM增大64.67%;当AM=6 mol/L

(MBA)/

(AM)=1.67×10

-4

(PVP)/

(AM)=7.51%时

制备的凝胶机械性能较好

拉伸强度达到1.84MPa

断裂伸长率可达3322%;随着含水率增加

凝胶拉伸强度及断裂伸长率均有所降低。

Abstract

The semi-interpenetrating polymer network (semi-IPN) of PAM/PVP hydrogels were synthesized by one-pot radical polymerization with PVP interpenetrated in chemical crosslinked polyacrylamide (PAM) hydrogel network which was initiated by ammonium potassium. The research was focused on the mechanical properties of PAM/PVP semi-IPN hydrogels. The results of FTIR

TGA coupled with tensile experiments demonstrate that hydrogen bond occurred between PAM and PVP. The tensile experiments show that tensile strength of hydrogel was improved through introducing PVP into PAM. Compared to pure chemical crosslinked PAM hydrogel

a 64.67% increase in tensile strength improvement was achieved with the addition of 7.51% of

(PVP)/

(AM). The mechanical properties were better in presence of AM 6mol/L with

(MBA)/

(AM) and

(PVP)/

(AM) of 1.67×10

-4

and 7.51% respectively

showing tensile strength of 1.84MPa and elongation of 3327%. With the increase of water content in hydrogel

both tensile strength and elongation were reduced.

关键词

氢键半互穿网络力学性能丙烯酰胺聚乙烯吡咯烷酮

Keywords

Hydrogen bondSemi-IPNMechanical propertiesAcrylamidePolyvinylpurrolidone

references

更多指标>

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

熔融沉积成型3D打印聚醚醚酮工艺优化研究进展

热、力及其复合外场原位辅助熔融沉积成型技术研究进展

超分子聚合物增强增韧的羧基丁腈橡胶

氨基甲酸酯基/脲键对混合TDI聚酯-聚氨酯树脂羰基氢键作用的影响

FRP高温力学性能研究进展