纳米Al<sub>2</sub>O<sub>3</sub>改性双酚A型环氧丙烯酸酯的制备与性能研究

王晓飞; 王虎; 赵凯锋; 张士玉; 白亚朋; 魏燕彦

doi:10.14028/j.cnki.1003-3726.2017.05.007

您当前的位置：

首页 >

文章列表页 >

纳米Al₂O₃改性双酚A型环氧丙烯酸酯的制备与性能研究

研究简报 | 更新时间：2022-09-06

- 纳米Al₂O₃改性双酚A型环氧丙烯酸酯的制备与性能研究
- Study on Preparation and Properties of Bisphenol-A Epoxy Acrylate Modified by Nano-Al₂O₃
- 高分子通报 2017年30卷第5期页码：53-61
- 作者机构：
  
  青岛科技大学高分子科学与工程学院，青岛 266042
- 作者简介：
  
  王晓飞(1991-)，女，在读硕士，研究方向为功能与特种高分子材料；
  *魏燕彦（1978-)，女，博士，副教授，硕士生导师，研究方向为3D打印光敏树脂、自修复聚氨酯、吸水膨胀丙烯酸酯橡胶等。E-mail：yywei@qust.edu.cn.
- 基金信息：
  
  山东省墙材革新与建筑节能科研开发项目([2013]357);青岛市城乡建设委员会建设事业科技发展专项(JK2014-4)
- DOI：10.14028/j.cnki.1003-3726.2017.05.007
  中图分类号：
- 纸质出版日期：2017-05-01，
  
  收稿日期：2016-11-07，
  
  修回日期：2017-02-13，
扫描看全文
王晓飞, 王虎, 赵凯锋, 张士玉, 白亚朋, 魏燕彦. 纳米Al₂O₃改性双酚A型环氧丙烯酸酯的制备与性能研究[J]. 高分子通报, 2017,30(5):53-61.

Xiao-fei WANG, Hu WANG, Kai-feng ZHAO, Shi-yu ZHANG, Ya-peng BAI, Yan-yan WEI. Study on Preparation and Properties of Bisphenol-A Epoxy Acrylate Modified by Nano-Al₂O₃[J]. Polymer Bulletin, 2017,30(5):53-61.
王晓飞, 王虎, 赵凯锋, 张士玉, 白亚朋, 魏燕彦. 纳米Al₂O₃改性双酚A型环氧丙烯酸酯的制备与性能研究[J]. 高分子通报, 2017,30(5):53-61. DOI： 10.14028/j.cnki.1003-3726.2017.05.007.

Xiao-fei WANG, Hu WANG, Kai-feng ZHAO, Shi-yu ZHANG, Ya-peng BAI, Yan-yan WEI. Study on Preparation and Properties of Bisphenol-A Epoxy Acrylate Modified by Nano-Al₂O₃[J]. Polymer Bulletin, 2017,30(5):53-61. DOI： 10.14028/j.cnki.1003-3726.2017.05.007.

摘要

选用硅烷偶联剂KH570对纳米Al

进行表面改性处理，并用改性后的Al

对双酚A环氧丙烯酸酯进行复合改性，研究了纳米Al

含量(1 % ( wt)~5% ( wt) )对树脂性能的影响。结果表明：改性纳米 Al

质量分数为5%时的复合材料的体积收缩率最小，为6.48%；粒子质量分数为2%时，树脂的凝胶率最大，为88.3%；热失重测试结果表明

改性纳米Al

提高了树脂的热稳定性；拉伸性能显示，随着改性纳米 Al

质量分数的增加，复合材料的拉伸强度先升高后下降，当改性纳米Al

质量分数为3%时，复合树脂拉伸强度最大，为34. 74MPa，与未改性树脂相比，拉伸强度提高了 108.27%。本文所制备的改性光敏树脂可适用于3D打印环境。

Abstract

In this paper

nano-Al

was modified by modifier KH570

and the modified Al

was used for the modification of bisphenol A epoxy acrylate. We studied the effect of the mass fraction of the modified nano-Al

(1 % (wt) ~5%(wt))on the properties of the resin. The results showed that the smallest volume shrinkage rate was 6. 48% when the connection of modified nano-Al

was 5 % ( wt) ; the highest gelling percent was 88. 3 % when the mass fraction of modified nano-Al

was 2 %. TGA test results showed that nano-Al

improves the thermal stability of the resin. Tensile results showed that with the increase of the mass fraction of the modified nano-Al

the tensile strength of the composite first increased and then decreased

and the tensile strength was the highest when the mass fraction of modified nano-Al

was 3%(the tensile strength was 34. 74MPa and increased by 108. 27%). The originality of this paper is that

first

we used modifier KH570 to modify the surface of nano-Al

making it easier to disperse in the resin matrix. Second

this modified photosensitive resin is suitable for 3D printing environment.

关键词

UV固化纳米Al2O3硅烷偶联剂KH570双酚A环氧丙烯酸酯3D打印

Keywords

UV curingNano-Al2O3Modifier KH570Bisphenol A epoxy acrylate3D printing

references

更多指标>

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

3D 打印聚酰亚胺研究进展

不同物理状态植物纤维/聚合物复合材料的3D 打印研究

3D打印海藻酸钠基功能材料的研究进展

CAD-CAE及3D 打印在《塑料制品设计》课程教学中的应用探索

植物纤维及其提取物增强聚合物的3D 打印成型研究

纳米Al2O3改性双酚A型环氧丙烯酸酯的制备与性能研究

Study on Preparation and Properties of Bisphenol-A Epoxy Acrylate Modified by Nano-Al2O3

DOI：10.14028/j.cnki.1003-3726.2017.05.007

摘要

Abstract

关键词

Keywords

references

纳米Al₂O₃改性双酚A型环氧丙烯酸酯的制备与性能研究

Study on Preparation and Properties of Bisphenol-A Epoxy Acrylate Modified by Nano-Al₂O₃