改性硅藻土／橡胶复合材料的结构与性能

武卫莉; 丛松岩

doi:10.14028/j.cnki.1003-3726.2019.08.006

您当前的位置：

首页 >

文章列表页 >

改性硅藻土／橡胶复合材料的结构与性能

研究简报 | 更新时间：2022-09-02

- 改性硅藻土／橡胶复合材料的结构与性能
- Structure and Properties of Modified Diatomite/Rubber Composites
- 高分子通报 2019年32卷第8期页码：35-40
- 作者机构：
  
  齐齐哈尔大学　材料科学与工程学院，齐齐哈尔 161006
- 作者简介：
  
  *武卫莉（1961 —），女，安徽六安人，博士，教授，硕士生导师，主要从事橡胶材料加工改性及其复合材料的研究，已发表论文100余篇。E-mail: wuweili2001@163.com.
- 基金信息：
- DOI：10.14028/j.cnki.1003-3726.2019.08.006
  中图分类号：
- 纸质出版日期：2019-08-20，
  
  收稿日期：2019-01-06，
  
  修回日期：2019-05-17，
扫描看全文
武卫莉, 丛松岩. 改性硅藻土／橡胶复合材料的结构与性能[J]. 高分子通报, 2019,32(8):35-40.

Wei-li WU, Song-yan CONG. Structure and Properties of Modified Diatomite/Rubber Composites[J]. Polymer Bulletin, 2019,32(8):35-40.
武卫莉, 丛松岩. 改性硅藻土／橡胶复合材料的结构与性能[J]. 高分子通报, 2019,32(8):35-40. DOI： 10.14028/j.cnki.1003-3726.2019.08.006.

Wei-li WU, Song-yan CONG. Structure and Properties of Modified Diatomite/Rubber Composites[J]. Polymer Bulletin, 2019,32(8):35-40. DOI： 10.14028/j.cnki.1003-3726.2019.08.006.

摘要

通过力学性能、扫描电镜（SEM）、红外光谱（IR)、X射线电子能谱（XPS）和热重（TG）分析，探讨改性硅藻土适合橡胶种类及对橡胶结构及热稳定性的影响，并与炭黑及白炭黑进行了对比研究。结果显示：改性硅藻土对氟橡胶（FKM）、丙烯酸酯橡胶（ACM）、三元乙丙橡胶（EPDM）、天然橡胶（NR）以及氯丁橡胶（CR）有增强作用，相容性较好，其中对FKM改性效果最明显，与白炭黑相比，其拉伸强度、扯断伸长率和耐磨性分别提高了28%、17%和30%；EPDM的拉伸强度、扯断伸长率和耐磨性分别提高了11%、12％和14%。并且改性硅藻土能够改善FKM和EPDM的耐热性能。

Abstract

The influence on the structure and thermal stability of the rubbers were studied by the mechanical properties

scanning electron microscopy (SEM)

infrared spectra (IR)

X-ray photoelectron (XPS) and thermogravimetric analysis(TG)

and compared with carbon black and silica. The results showed that the modified diatomite had good reinforcing effect on fluorine rubber (FKM)

acrylic rubber (ACM)

ethylene propylene diene monomer rubber (EPDM)

natural rubber (NR) and chloroprene rubber (CR)

the compatibility between the modified diatomite and the rubbers was good

and the modified effect for the FKM was the best in all rubber. Compared with the silica

the tensile strength

elongation at break and wear resistance of the FKM were increased by 28%

17% and 30%

respectively

and the EPDM was increased 11%

12%

and 14%

respectively. And the modified diatomite could improved the thermal properties of FKM and EPDM.

关键词

硅藻土橡胶复合材料机械性能结构

Keywords

DiatomiteRubberCompositesMechanical propertiesStructure

references

更多指标>

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

硅藻土增强橡胶复合材料的研究进展

一种新型硅藻土填充橡胶纳米复合材料研究

由橡胶材料看高分子物理知识点的综合运用

微纤化纤维素增强聚合物基复合材料研究进展

木质素在橡胶中的应用研究进展