g-C<sub>3</sub>N<sub>4</sub>/偕胺肟纤维的制备及光催化降解罗丹明B染料

陶庭先; 王曼玲; 卢晓韩; 陈丽茹; 张苗; 吴之传

doi:10.14028/j.cnki.1003-3726.2020.10.007

您当前的位置：

首页 >

文章列表页 >

g-C₃N₄/偕胺肟纤维的制备及光催化降解罗丹明B染料

研究简报 | 更新时间：2022-08-31

- g-C₃N₄/偕胺肟纤维的制备及光催化降解罗丹明B染料
- Preparation of g-C₃N₄/Amidoxime Fibers and Photocatalytic Degradation of Rhodamine B
- 高分子通报 2020年33卷第10期页码：56-65
- 作者机构：
  
  安徽工程大学生物与化学工程学院,芜湖 241000
- 作者简介：
  
  陶庭先(1963-),男,硕士,教授,研究方向为高分子纳米复合材料。E-mail:tw3@ahpu.edu.cn;
  * 吴之传(1963-),女,硕士,教授,研究方向为高分子金属配合物。E-mail:wuzhichuan@ahpu.edu.cn.
- 基金信息：
  
  国家自然科学基金资助项目(21571003)
- DOI：10.14028/j.cnki.1003-3726.2020.10.007
  中图分类号：
- 纸质出版日期：2020-10-20，
  
  收稿日期：2019-10-11，
  
  修回日期：2020-05-30，
扫描看全文
陶庭先, 王曼玲, 卢晓韩, 陈丽茹, 张苗, 吴之传. g-C₃N₄/偕胺肟纤维的制备及光催化降解罗丹明B染料[J]. 高分子通报, 2020,33(10):56-65.

Ting-xian TAO, Man-ling WANG, Xiao-han LU, Li-ru CHEN, Miao ZHANG, Zhi-chuan WU. Preparation of g-C₃N₄/Amidoxime Fibers and Photocatalytic Degradation of Rhodamine B[J]. Polymer Bulletin, 2020,33(10):56-65.
陶庭先, 王曼玲, 卢晓韩, 陈丽茹, 张苗, 吴之传. g-C₃N₄/偕胺肟纤维的制备及光催化降解罗丹明B染料[J]. 高分子通报, 2020,33(10):56-65. DOI： 10.14028/j.cnki.1003-3726.2020.10.007.

Ting-xian TAO, Man-ling WANG, Xiao-han LU, Li-ru CHEN, Miao ZHANG, Zhi-chuan WU. Preparation of g-C₃N₄/Amidoxime Fibers and Photocatalytic Degradation of Rhodamine B[J]. Polymer Bulletin, 2020,33(10):56-65. DOI： 10.14028/j.cnki.1003-3726.2020.10.007.

摘要

采用高温煅烧三聚氰胺的方法来制备g-C

并以偕胺肟纤维作为载体

结合水浴法制备了廉价易得、催化活性高、无毒无害且易回收的g-C

/AOCF复合催化材料。通过XRD、SEM、FT-IR、XPS、UV-VISDRS等手段对样品进行表征分析

其中SEM 表征结果显示g-C

均匀分布在纤维表面

呈无定形态

XPS和FT-IR表征结果证实g-C

与AOCF之间存在强相互作用。在紫外光的照射下

以降解罗丹明B染料来考察催化材料的催化活性

结果表明

当g-C

添加量为3g/L

在30℃的水浴温度下反应2h所制备的g-C

/AOCF复合催化剂光催化活性最佳

重复性实验表明该催化剂具有较好的稳定性

且光催化反应过程符合一级反应动力学规律。

Abstract

In this paper

g-C

was prepared by calcining melamine at high temperature

and g-C

/AOCF monolithic composite catalytic material was prepared with amidoxime fiber as carrier and water bath method

which is cheap

easy to get

high catalytic activity

non-toxic

harmless and easy to recover. The samples were characterized by XRD

SEM

FT-IR

XPS

UV-Vis DRS

etc. the SEM results showed that g-C

was uniformly distributed on the surface of the fiber

showing an amorphous morphology. The XPS and FT-IR results confirmed that there was a certain chemical bond between g-C

and aocf. Under UV irradiation

the catalytic activity of the catalytic material was investigated by degradation of Rhodamine B dye. The results showed that when the addition of g-C

was 3 g/L

the reaction was carried out at 30℃ in water bath The g-C

/AOCF composite catalyst prepared by H has the best photocatalytic activity. The repeatability experiment shows that the catalyst has good stability and the photocatalytic reaction process conforms to the first-order reaction kinetics.

关键词

g-C3N4/偕胺肟纤维高温煅烧-水浴法光催化降解罗丹明B

Keywords

g-C3N4/Amidoxime fiberHigh temperature calcination-water bath methodPhotocatalytic degradationRhodamine B

references

更多指标>

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

三维磁性复合材料ZnFe₂O₄/g-C₃N₄/rGO@Ag的制备及高效光催化降解罗丹明B的研究

罗丹明B分子印迹聚合物微球的制备及其荧光光谱机理的研究

g-C3N4/偕胺肟纤维的制备及光催化降解罗丹明B染料

Preparation of g-C3N4/Amidoxime Fibers and Photocatalytic Degradation of Rhodamine B

DOI：10.14028/j.cnki.1003-3726.2020.10.007

摘要

Abstract

关键词

Keywords

references

g-C₃N₄/偕胺肟纤维的制备及光催化降解罗丹明B染料

Preparation of g-C₃N₄/Amidoxime Fibers and Photocatalytic Degradation of Rhodamine B