相分离法制备聚碳酸酯/聚乳酸复合微球与调控

邱丽清; 刘杭忠; 刘俊劭

doi:10.14028/j.cnki.1003-3726.2021.07.008

您当前的位置：

首页 >

文章列表页 >

相分离法制备聚碳酸酯/聚乳酸复合微球与调控

研究简报 | 更新时间：2022-08-30

- 相分离法制备聚碳酸酯/聚乳酸复合微球与调控
- Preparation and Control of PC/PLA Composite Microsphere via Phase Separation
- 高分子通报 2021年34卷第7期页码：65-70
- 作者机构：
  
  武夷学院生态与资源工程学院,福建省竹材工程技术研究中心,福建省生态产业绿色技术重点实验室,武夷山 354300
- 作者简介：
  
  * 邱丽清,女,博士在读,讲师,主要从事生物质资源和高分子材料的研究与应用。E-mail: wuyi_qlq@163.com.
- 基金信息：
  
  福建省中青年教师教育科研项目(JAT190764);福建省自然科学基金项目(2018J01518)
- DOI：10.14028/j.cnki.1003-3726.2021.07.008
  中图分类号：
- 纸质出版日期：2021-07-20，
  
  收稿日期：2020-04-16，
  
  修回日期：2021-01-22，
扫描看全文
邱丽清, 刘杭忠, 刘俊劭. 相分离法制备聚碳酸酯/聚乳酸复合微球与调控[J]. 高分子通报, 2021,34(7):65-70.

Li-qing QIU, Hang-zhong LIU, Jun-shao LIU. Preparation and Control of PC/PLA Composite Microsphere via Phase Separation[J]. Polymer Bulletin, 2021,34(7):65-70.
邱丽清, 刘杭忠, 刘俊劭. 相分离法制备聚碳酸酯/聚乳酸复合微球与调控[J]. 高分子通报, 2021,34(7):65-70. DOI： 10.14028/j.cnki.1003-3726.2021.07.008.

Li-qing QIU, Hang-zhong LIU, Jun-shao LIU. Preparation and Control of PC/PLA Composite Microsphere via Phase Separation[J]. Polymer Bulletin, 2021,34(7):65-70. DOI： 10.14028/j.cnki.1003-3726.2021.07.008.

摘要

聚碳酸酯(PC)、聚乳酸(PLA)及三氯甲烷(CHCl

)混合作为油相

聚乙烯醇(PVA)溶液作为水相

通过相分离法制备PC/PLA复合微球。研究CHCl

浓度、水油比、PVA质量分数及PC/PLA质量配比对形成的PC/PLA复合微球形貌、结构的影响。实验结果表明:最佳的相分离实验条件为CHCl

浓度为2g/mL、水油比为4∶1、PVA质量分数为1%及PC/PLA质量配比为1/1时通过SEM 观察到粒径分布均匀、规则、光滑的复合微球。在适宜的条件下

PC和PLA分子链间作用力相当

扩散能力强

协同一致地结晶

促进成核-结晶而制备PC/PLA复合微球。

Abstract

The mixture of Polycarbonate (PC)

polylactic acid (PLA) and trichloromethane (CHCl

) were accounted for the oil phase and polyvinyl alcohol (PVA) solution was acted as the aqueous phase

which were prepared by phase separation for PC/ PLA composite microspheres. The factors of CHCl

concentration

water-oil ratio

PVA mass fraction and PC/PLA ratio on the morphology and structure were investigated. The results showed that the composite microspheres with small particle size

uniform distribution and surface are formed when the concentration of CHCl

was 2g/mL

water/oil mass ratio was 4∶1

PVA mass fraction was 1% and PC/PLA mass ratio are 1/1. Under the appropriate conditions

PC and PLA intermolecular chains have the same intermolecular force and strong diffusion ability

and the PC/PLA composite microspheres are prepared by synergistic and consistent crystallization

which promotes nucleation-crystallization.

关键词

聚碳酸酯聚乳酸复合微球相分离

Keywords

PolycarbonatePoly(lactic acid)Composite microspherePhase separation

references

更多指标>

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

一种推导相分离热力学中

χ^{c}

与

ϕ^{c}

的方法

数形结合讲解高分子溶液的相分离

以热点问题为导向的高分子物理综合实验设计

对高分子物理学中混合自由能-组成曲线与相图的讨论

聚碳酸酯Fries重排与流变行为的关联研究