脂肪酶催化合成纤维素-甲基丙烯酸丁酯接枝聚合吸油材料

哈丽丹·买买提; 阿不利米提; 库尔班江·肉孜; 阿里木江

doi:10.14028/j.cnki.1003-3726.2011.05.013

您当前的位置：

首页 >

文章列表页 >

脂肪酶催化合成纤维素-甲基丙烯酸丁酯接枝聚合吸油材料

研究简报 | 更新时间：2022-09-18

- 脂肪酶催化合成纤维素-甲基丙烯酸丁酯接枝聚合吸油材料
- Synthesis of Cellulose-Poly (BMA) Graft Copolymer Oil Absorbing Resins with Lipase as Catalyze
- 高分子通报 2011年24卷第5期页码：67-75
- 作者机构：
  
  新疆大学化学化工学院，乌鲁木齐　830046
- 作者简介：
  
  哈丽丹·买买提（1966－），女，副教授，主要研究方向为高分子材料。E-mail：Halidan2000@yahoo.com.cn.
- 基金信息：
  
  新疆乌鲁木齐市科技局“种子基金”资助项目(K08141015)
- DOI：10.14028/j.cnki.1003-3726.2011.05.013
  中图分类号：
- 纸质出版日期：2011-05，
扫描看全文
哈丽丹·买买提, 阿不利米提, 库尔班江·肉孜, 阿里木江. 脂肪酶催化合成纤维素-甲基丙烯酸丁酯接枝聚合吸油材料[J]. 高分子通报, 2011,24(5):67-75.

MAMAT Halidan, Ablimit, ROUZI Kurbanjian, Alimjian. Synthesis of Cellulose-Poly (BMA) Graft Copolymer Oil Absorbing Resins with Lipase as Catalyze[J]. Polymer Bulletin, 2011,24(5):67-75.
哈丽丹·买买提, 阿不利米提, 库尔班江·肉孜, 阿里木江. 脂肪酶催化合成纤维素-甲基丙烯酸丁酯接枝聚合吸油材料[J]. 高分子通报, 2011,24(5):67-75. DOI： 10.14028/j.cnki.1003-3726.2011.05.013.

MAMAT Halidan, Ablimit, ROUZI Kurbanjian, Alimjian. Synthesis of Cellulose-Poly (BMA) Graft Copolymer Oil Absorbing Resins with Lipase as Catalyze[J]. Polymer Bulletin, 2011,24(5):67-75. DOI： 10.14028/j.cnki.1003-3726.2011.05.013.

摘要

以棉浆粕为基材

硝酸铈铵／HNO

为引发剂

甲基丙烯酸丁酯（BMA）为接枝单体

脂肪酶为催化剂

′-亚甲基双丙烯酰胺为交联剂

采用悬浮震荡接枝聚合反应制备了纤维素-BMA 接枝聚合吸油材料。采用红外光谱、X 射线衍射、扫描电镜、热重、差热等手段对产物结构进行了表征

考察了棉浆粕的引发及其后的接枝聚合反应

得到脂肪酶催化合成纤维素-BMA 接枝聚合吸油材料的最佳工艺条件为：棉浆粕用含有铈粒子的0.15mol／L 的HNO

水溶液

在45℃活化处理2.5h 后

在脂肪酶催化剂下

与BMA 发生接枝聚合反应。反应物质量比为纤维素／引发剂／单体／脂肪酶／交联剂＝1／0.03／1.5／0.02／0.02

反应温度50℃

反应时间 24h。在上述工艺条件下

所得纤维素-BMA 的接枝聚合物有较高的接枝率及理想的吸油性能。

Abstract

The cellulose-poly (BMA) graft copolymer oil absorption resins has been synthesized from butyl methacrylate modified cotton pulp (cellulose) which initiated with ceric ion /HNO

solution by shake graft copolymerization using porcine pancreatic lipase as catalyze

′-methylene-bisacrylamide as crosslinker.Structure of the cellulose-poly (BMA) graft copolymer was characterized by means of FT-IR、XRD、SEM、TG、DSC etc.Effects of the process of initiating cotton pulp and graft copolymerization condition were investigated.The ideal cellulose-poly (BMA) graft copolymer oil absorption resins could be prepared when the cotton pulp initiated with 0.15mol/LHNO

solution of containats ceric ion at 45℃ for 2.5h

then reacted with BMA by using porcine pancreatic lipase as catalyze

′-methylene-bis-acrylamide as crosslinker.Under the optimal conditions of m (cellulose): m (initiator): m (monomer): m (porcine pancreatic lipase): m (crosslinker) =1∶0.03∶1.5∶0.02∶0.02

50℃ and 24h

the graft yield and oil pick-up abilities of the synthesized cellulose-poly (BMA) graft copolymer oil absorption resins are choiceness.

关键词

脂肪酶纤维素甲基丙烯酸丁酯接枝聚合吸油材料

Keywords

Porcine pancreatic lipaseCelluloseButyl methacrylateGraft copolymerizationOil absorption resins

references